ABS TR-557I
58
- Properties:wear resistanthigh strengthHigh impact resistanceHigh temperature resistanHigh impact
- Usages:Automotive components
Compare
View PricesTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Shrinkage rate | ASTM D-955 | 0.4～0.7 % | |
| melt mass-flow rate | ASTM D624 | 2.0 g/10min |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ASTM D-785 | 105 | ||
| bending strength | ASTM D-790 | 630(62) kg/cm2(MPa) | |
| Tension measurement | ASTM D-638 | 17800(1740) kg/cm2(MPa) | |
| Stretching rate (resistance point) | ASTM D-638 | ≥6 % | |
| Stretching rate (breaking point) | ASTM D-638 | 50 % | |
| Tensile strength | ASTM D-638 | 430(42) kg/cm2(MPa) | |
| Bending modulus | ASTM D-790 | 20500（2000） kg/cm2(MPa) | |
| IZOD impact strength | ASTM D-256 | 15(150) kg.cm/cm(J/m) |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| combustibility | IEC707 | - mm/min | |
| Hot deformation temperature | ASTM D-648 | 89(88) °C | |
| combustibility | UL-94 | HB CLASS | |
| Microcard softening point | ASTM D-1525 | 98(93) °C | |
| ASTM D-648 | 95(90) °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.