PFA NEOFLON® AP-210-J DAIKIN JAPAN

123

Properties:
Weather resistance
Flame retardant
Usages:
Wire sheath
Compare
View Prices

Technical Data Sheet

physical property	Test Condition	Test Method	Test Result	Unit
Apparent density		JISK6891	1.00到1.40	g/cm³
Melt mass flow rate	372°C/5.0kg	ASTMD1238	10到17	g/10min
Water absorption rate	饱和	ASTMD570	<0.010	%

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Shore hardness	邵氏D	ASTMD2240	60到70
tensile strength	屈服	JISK6891	25.4到30.4	Mpa
elongation	断裂	JISK6891	350到450	%
Bending modulus		ASTMD790	580到690	Mpa
Compressive modulus		ASTMD695	490到590	Mpa
compressive strength	1%应变	ASTMD695	4.90到5.90	Mpa
	compressive strength	25%应变	ASTMD695	31.4到33.3	Mpa
	compressive strength	compressive strength	摩擦系数(与钢-静态)	ASTMD695	0.040到0.050
Load deformation	25°C,14MPa2	ASTMD621	2.50到3.00	%
	Load deformation	25°C,14MPa3	ASTMD621	8.00到9.00	%
		Load deformation	100°C,6.9MPa2	ASTMD621	2.00到3.00	%
		Load deformation	Load deformation	100°C,6.9MPa3	ASTMD621	8.50到9.50	%
Flexural Strength		ASTMD790	Nobreak

Thermal performance	Test Condition	Test Method	Test Result	Unit
Melting temperature		ASTMD4591	300到310	°C
Linear coefficient of thermal expansion	MD：20到100°C	ASTMD696	1.2E-04	cm/cm/°C
specific heat			1050	J/kg/°C
thermal conductivity		ASTMC177	0.26	W/m/K

Filling analysis	Test Condition	Test Method	Test Result	Unit
Melt viscosity	380°C		2.00E+6到2.50E+7	mPa·s

flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating	1.6mm	UL94	V-0
Extreme Oxygen Index	1.57mm	ASTMD2863	>95	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.