PCT Thermx® TE4005 CELANESE USA
0
- Properties:Fillerglass mineral33%filler by weight
CompareTechnical Data Sheet
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 1.8MPa,未退火 | ISO 75-2/A | 230 °C |
| melting temperature | ISO 11357-3 | 285 °C |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ISO 1183 | 1.45 g/cm³ | |
| shrinkage rate | TD | ISO 294-4 | 0.52 % |
| density | ISO 1183 | 1.45 g/cm3 | |
| shrinkage rate | MD | ISO 294-4 | 0.28 % |
| tensile modulus | ISO 527-2/1A/1 | 9000 MPa | |
| tensile strength | Break | ISO 527-2/1A/5 | 110 MPa |
| Tensile strain | Break | ISO 527-2/1A/5 | 1.8 % |
| Charpy Notched Impact Strength | 23℃ | ISO 179/1eU | 40 kJ/m2 |
| Thermal performance | 热变形温度，1.8 MPa, 未退火 | ISO 75-2/A | 230 ℃ |
| melting temperature | ISO 11357-3 | 285 ℃ |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| dielectric strength | IEC 60243-1 | 46 kV/mm | |
| IEC 60243-1 | 46 kV/mm |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile modulus | ISO 527-2/1A/1 | 9000 MPa | |
| tensile strength | Break | ISO 527-2/1A/5 | 110 MPa |
| Tensile strain | Break | ISO 527-2/1A/5 | 1.8 % |
| impact performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 40 kJ/m² |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.