PPS A305M TORAY JAPAN

Form：Granules | Grade：Injection grade

Properties:

High temperature resistanhigh strengthFlame retardantFiller: Glass mineral50% filler by weight

Typical Applications:

Electrical appliancesSports EquipmentAutomotive sectorElectronic fieldElectrical field

Supplier(1)

Product Description

Certificates(1)

Datasheet

Product Description

Typical Applications:	Electrical appliances \| Sports Equipment \| Automotive sector \| Electronic field \| Electrical field
Properties:	High temperature resistan \| high strength \| Flame retardant \| Filler: Glass mineral \| 50% filler by weight

Certificates

Technical Data Sheet

other	Test Condition	Test Method	Test Result	Test Unit
characteristic			高强度.流动性
Color			本色.黑
impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch	23°C	ISO 179	40	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	0.35mm	UL 94	V-0
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
tensile strength		ASTM D638/ISO 527	140	kg/cm²(MPa)[Lb/in²]
Rockwell hardness		ASTM D785	122
Bending modulus		ASTM D790/ISO 178	190	kg/cm²(MPa)[Lb/in²]
bending strength		ASTM D790/ISO 178	220	kg/cm²(MPa)[Lb/in²]
Elongation at Break		ASTM D638/ISO 527	0.9	%
Charpy Notched Impact Strength		ASTM D256/ISO 179	740	kg·cm/cm(J/M)ft·lb/in
Charpy Notched Impact Strength	Charpy Notched Impact Strength		ASTM D256/ISO 179	8	kg·cm/cm(J/M)ft·lb/in
bending strength	23°C	ISO 178	260	Mpa
Bending modulus	23°C	ISO 178	17000	Mpa
Tensile strain	Break,23°C	ISO 527-2	1.3	%
tensile strength	Yield,23°C	ISO 527-2	180	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Linear coefficient of thermal expansion	TD	ISO 11359-2	3E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD	ISO 11359-2	1.8E-05	cm/cm/°C
Melting temperature		ISO 11357-3	278	°C
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	260	°C
Combustibility (rate)		UL 94	V-0
Hot deformation temperature	HDT	ASTM D648/ISO 75	>260	℃（℉）
Melting temperature			278	℃（℉）
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	23°C,24hr	ISO 62	0.020	%
Shrinkage rate	MD:3.00mm4	Internal Method	0.16	%
Shrinkage rate	Shrinkage rate	TD:3.00mm2	Internal Method	0.75	%
density		ASTM D792/ISO 1183	1.85
Shrinkage rate		ASTM D955	0.16	%
Water absorption rate		ASTM D570/ISO 62	0.02	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Volume resistivity		ASTM D257/IEC 60093	1014	Ω.cm
Dielectric constant		ASTM D150/IEC 60250	5
Dielectric strength		IEC 60243-1	24	KV/mm
Volume resistivity		IEC 60093	1E+16	ohms·cm
Dissipation factor	23°C,1MHz	IEC 60250	2E-03
Dielectric constant	23°C,1MHz	IEC 60250	5.00
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	R-Scale	ISO 2039-2	122
Supplementary Information	Test Condition	Test Method	Test Result	Test Unit
BarFlowLength	320°C,1.00mm	Internal Method	120	mm

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.