Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792 | 1.30 g/cm³ |
| melt mass-flow rate | | ASTM D1238 | 7.0 g/10min |
| Water absorption rate | | ASTM D570 | 0.20 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | M-Scale | ASTM D785 | 92 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| Limiting Oxygen Index | | ASTM D2863 | 38 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | Yield | ISO 527-2/1A/50 | 89.0 MPa |
| tensile strength | | ASTM D638 | 92.0 MPa |
| elongation | | ASTM D638 | 6.0 % |
| elongation | Yield | ISO 527-2/1A/50 | 5.4 % |
| elongation | | ASTM D638 | 50to80 % |
| elongation | Break | ISO 527-2/1A/50 | 50to80 % |
| Flexural modulus | | ASTM D790 | 320 MPa |
| Flexural modulus | | ISO 178 | 3300 MPa |
| bending strength | | ASTM D790 | 127 MPa |
| bending strength | | ISO 178 | 128 MPa |
| shear strength | | ASTM D732 | 79.0 MPa |
| compressive strength | | ASTM D695 | 110 MPa |
| Tensile modulus | | ASTM D638 | 3300 MPa |
| Tensile modulus | | ISO 527-2/1A/1 | 3400 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256 | 91 J/m |
| Impact strength of cantilever beam gap | | ISO 180 | 7.0 kJ/m² |
| Suspended wall beam without notch impact strength | | ASTMD4812 | 无断裂 |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | ASTM D257 | >1.9E+17 ohms |
| Volume resistivity | | ASTM D257 | 6.2E+17 ohms·cm |
| dielectric strength | | ASTM D149 | 180 kV/mm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D648 | 181 °C |
| Glass Transition Temperature | | ASTM D3418 | 158 °C |
| melting temperature | | ASTM D3418 | 340 °C |
| specific heat | | DSC | 1390 J/kg/°C |
| specific heat | | DSC | 1960 J/kg/°C |
| thermal conductivity | | ASTME1530 | 0.23 W/m/K |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.