Technical Data Sheet
| thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat Deflection Temperature | 0.45MPa,未退火 | ISO 75-2/B | 270 °C |
| Heat Deflection Temperature | 1.8MPa,未退火 | ISO 75-2/A | 250 °C |
| melting temperature | | ISO 11357-3 | 285 °C |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 6E-06 cm/cm/°C |
| Linear coefficient of thermal expansion | TD | ISO 11359-2 | 1E-04 cm/cm/°C |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | 1.5mm | UL 94 | V-0 |
| UL flame retardant rating | 0.8mm | UL 94 | V-2 |
| Physical properties | Test Condition | Test Method | Test Result |
|---|
| shrinkage rate | TD | ISO 294-4 | 0.80 % |
| shrinkage rate | MD | ISO 294-4 | 0.30 % |
| water absorption rate | 饱和,23°C | ISO 62 | 0.90 % |
| water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.15 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| dielectric strength | | IEC 60243-1 | 33 KV/mm |
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 1 |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile modulus | | ISO 527-2/1A/1 | 10800 Mpa |
| tensile strength | 断裂 | ISO 527-2/1A/5 | 114 Mpa |
| Tensile strain | 断裂 | ISO 527-2/1A/5 | 1.5 % |
| flexural modulus | 23°C | ISO 178 | 10000 Mpa |
| bending strength | 23°C | ISO 178 | 172 Mpa |
| Rockwell hardness | M级 | ISO 2039-2 | 119 |
| impact performance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 30 kJ/m² |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.