Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| melt mass-flow rate | | ASTMD1238 | 25 g/10min |
| Shrinkage rate 4 | | ASTMD955 | 0.70到0.90 % |
| Shrinkage rate 4 | | ASTMD955 | 1.0到1.2 % |
| Water absorption rate | | ASTMD570 | 0.20 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ASTMD785 | 94 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | V-0 |
| UL flame retardant rating | | UL94 | V-0 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ASTMD638 | 3000 Mpa |
| Tensile modulus | | ISO527-2/1A/1 | 3200 Mpa |
| Tensile stress | | ISO527-2/1A/50 | 89.0 Mpa |
| shear strength | | ASTMD732 | 78.0 Mpa |
| Tensile stress | | ASTMD638 | 87.0 Mpa |
| elongation | | ASTMD638 | 6.2 % |
| elongation | | ISO527-2/1A/50 | 5.7 % |
| elongation | | ASTMD638 | >40 % |
| elongation | | ISO527-2/1A/50 | >40 % |
| Flexural modulus | | ASTMD790 | 3100 Mpa |
| Flexural modulus | | ISO178 | 3200 Mpa |
| bending strength | | ASTMD790 | 124 Mpa |
| bending strength | | ISO178 | 127 Mpa |
| compressive strength | | ASTMD695 | 112 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Suspended wall beam without notch impact strength | | ASTMD256,ISO180 | 无断裂 |
| Filling analysis | Test Condition | Test Method | Test Result |
|---|
| melt viscosity | | ASTMD3835 | 240 Pa·s |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | ASTMD257 | >1.9E+17 ohms |
| Volume resistivity | | ASTMD257 | 5E+17 ohms·cm |
| dielectric strength | | ASTMD149 | 16 KV/mm |
| dielectric constant | | ASTMD150 | 3.10 |
| dielectric constant | | ASTMD150 | 3.12 |
| dielectric constant | | ASTMD150 | 3.10 |
| Dissipation Factor | | ASTMD150 | 1E-03 |
| Dissipation Factor | | ASTMD150 | 1E-03 |
| Dissipation Factor | | ASTMD150 | 4E-03 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| thermal conductivity | | ASTME1530 | 0.24 W/m/K |
| Hot deformation temperature 6 | | ASTMD648 | 190 °C |
| Glass Transition Temperature | | ASTMD3418 | 158 °C |
| | ASTMD3418 | 345 °C |
| | ASTME831 | 4.7E-05 cm/cm/°C |
| specific heat | | DSC | 1310 J/kg/°C |
| specific heat | | DSC | 1820 J/kg/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.