Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTMD1505 | 1.18 g/cm³ |
| Shrinkage rate | | ASTMD955 | 0.50to0.70 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | R-Scale | ASTMD785 | 111 |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| transmissivity | | ASTMD1003 | 91.0 % |
| Haze ratio | | ASTMD1003 | <1.0 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| bending strength | Yield | ASTMD790 | 64.0 MPa |
| Tensile modulus | | ASTMD638 | 1580 MPa |
| tensile strength | Yield | ASTMD638 | 43.0 MPa |
| tensile strength | Break | ASTMD638 | 52.0 MPa |
| elongation | Yield | ASTMD638 | 7.0 % |
| elongation | Break | ASTMD638 | 210 % |
| Flexural modulus | | ASTMD790 | 1580 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTMD256 | 860 J/m |
| GardnerImpact | | ASTMD5420 | 3.50 J |
| Impact strength of cantilever beam gap | | ASTMD4812 | NoBreak |
| film | Test Condition | Test Method | Test Result |
|---|
| Film thickness - tested | | | 130 µm |
| ElasticModulus-MD | | ASTMD882 | 979 MPa |
| tensile strength | | ASTMD882 | 56.5 MPa |
| elongation | | ASTMD882 | 220 % |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTMD648 | 94.0 °C |
| Heat distortion temperature | | ASTMD648 | 81.0 °C |
| Glass Transition Temperature | | DSC | 110 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.