Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | GB/T1033 | 1.52到1.82 g/cm³ |
| melt mass-flow rate | | GB/T3682 | 20到120 g/10min |
| Shrinkage rate | | | 0.30到0.50 % |
| Shrinkage rate | | | 0.20到0.40 % |
| Water absorption rate | | GB/T1034 | 0.20到0.40 % |
| PVLimit | | | 800到1600 |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | GB/T9342 | 80到120 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | V-0 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Bending stress | | GB/T1042 | 150 MPa |
| compression stress | | GB/T1041 | 200 MPa |
| | ASTMD1894 | 0.10到0.30 |
| Wear factor | | | 0.00200到0.100 mm³/kg/km |
| Tensile stress | | GB/T1040 | 125 MPa |
| Tensile strain | Break | GB/T1040 | 1.0 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | GB/T1043 | 10 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | GB/T1410 | 1.0E+10到1.0E+14 ohms |
| Volume resistivity | | GB/T1410 | 1.0E+10到1.0E+13 ohms·cm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | GB/T1634 | 245到270 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.