Technical Data Sheet
| Cured Properties | Test Condition | Test Method | Test Result |
|---|
| Dissipation Factor | | | 9E-03 |
| Shore hardness | | | 93 |
| LapShearStrength | | | 12.5 MPa |
| relative permittivity | | | 6.40 |
| Volume resistivity | | | >8.0E+13 ohms·cm |
| thermosetting | Test Condition | Test Method | Test Result |
|---|
| Thermosetting components | | | 100 |
| Thermosetting components | | | 按重量计算的混合比:2.2 |
| Thermosetting components | | | 26 wk |
| Uncured Properties | Test Condition | Test Method | Test Result |
|---|
| Color | | | Amber |
| Color | | | Grey |
| density | | | 1.02 g/cm³ |
| density | | | 2.44 g/cm³ |
| density | | | 20to40 Pa·s |
| density | | | 1.0 hr |
| density | Pot Life | | 360 min |
| physical property | Test Condition | Test Method | Test Result |
|---|
| Particle size | | | <50.0 µm |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| DegradationTemperature | | | 356 °C |
| Shear Strength | | | 46.9 MPa |
| operate temperature | | | -55-200 °C |
| operate temperature | | | -55-300 °C |
| operate temperature | | | 7.15 GPa |
| operate temperature | | | 2.50 |
| weight loss on heating | | | 0.11 % |
| weight loss on heating | | | 0.20 % |
| weight loss on heating | | | 0.45 % |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Linear coefficient of thermal expansion | | | 2.6E-05 cm/cm/°C |
| Linear coefficient of thermal expansion | | | 9.7E-05 cm/cm/°C |
| Linear coefficient of thermal expansion | | | 1.4 W/m/K |
| Glass Transition Temperature | | | >90.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.