PA6

PA6 LUBEMID B27 MB NATURAL LUBEN PLAST srl

Compare

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Suspended wall beam without notch impact strength	23°C	ISO 180	90to100 kJ/m²
Impact strength of cantilever beam gap	23°C	ISO 180/A	4.0to5.0 kJ/m²
	Impact strength of cantilever beam gap	23°C4	ASTM D256	3.5to4.5 kJ/m²
		Impact strength of cantilever beam gap	23°C3	ASTM D256	100to110 kJ/m²
		Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C,3.20mm	ASTM D256A	35to45 J/m
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	90to100 kJ/m²
Charpy Notched Impact Strength	23°C	ISO 179/1eA	4.0to5.0 kJ/m²

flammability	Test Condition	Test Method	Test Result
Burning wire flammability index	2.0mm	IEC 60695-2-12	750 °C

mechanical properties	Test Condition	Test Method	Test Result
Bending modulus		ISO 178	3000to3500 MPa
bending strength		ISO 178	70.0to80.0 MPa
Tensile strain	Break	ISO 527-2/1A/50	15to20 %
Tensile strain	Tensile strain	Yield	ISO 527-2/1A/50	8.0to10 %
tensile strength	Break	ISO 527-2/1A/50	50.0to60.0 MPa
tensile strength	tensile strength	Yield	ISO 527-2/1A/50	50.0to60.0 MPa
Tensile modulus		ISO 527-2/1A/1	3500to4000 MPa

thermal performance	Test Condition	Test Method	Test Result
Melting temperature		Internal Method	210to225 °C
Vicat softening temperature	--	ISO 306/B120	200to210 °C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/A120	205to215 °C
Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	55.0to65.0 °C
	Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	160to170 °C
	Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed,3.20mm	ASTM D648	115to165 °C

Physical properties	Test Condition	Test Method	Test Result
Water absorption rate	23°C,24hr,3.20mm	ISO 62	2.0 %
density		ISO 1183/A	1.12to1.16 g/cm³

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.