HDPE HD6070EA
61
- Properties:High temperature resistan
- Usages:plastic palletPlastic boxTraySeatMainly used for producing general hard objectsSuch as: Flat noodlesturnover boxbasketseat
CompareTechnical Data Sheet
| Basic performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | 6.5-8.0 g/10min | ||
| 6.0-9.0 g/10min | |||
| 5.5-9.5 g/10min | |||
| density | 955-960 kg/m | ||
| 955-960 kg/m | |||
| 954-964 kg/m |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| elongation at break | ≥900 % | ||
| Impact strength of cantilever beam gap | 5.0 KJ/m | ||
| 4.0 KJ/m | |||
| Flexural modulus | ≥1050 Mpa | ||
| ≥1000 Mpa | |||
| ≥900 Mpa | |||
| elongation at break | >=1300 % | ||
| tensile strength | ≥26 Mpa | ||
| ≥25 Mpa | |||
| ≥23 Mpa | |||
| elongation at break | ≥950 % | ||
| spiral flow length | 360 mm | ||
| Environmental stress cracking resistance | 55 (50°C)小时 | ||
| 25 (50°C)小时 | |||
| Impact strength of cantilever beam gap | 6.0 KJ/m | ||
| elongation at break | ≥800 % |
| Other performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| cleanliness | 0-20 个/kg | ||
| 21-40 个/kg | |||
| 41-60 个/kg | |||
| ash content | ≤0.03 % | ||
| ≤0.04 % | |||
| ≤0.05 % | |||
| Cleanliness (color particles) | 0-5 个/kg | ||
| 6-10 个/kg | |||
| 10-20 个/kg |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| vicat | 127 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.