Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| melt mass-flow rate | | ISO1133 | 15 g/10min |
| Melt volume flow rate | | ISO1133 | 14.0 cm3/10min |
| Shrinkage rate | | | 0.50to0.70 % |
| Shrinkage rate | | | 0.50to0.70 % |
| Shrinkage rate | | | 0.24 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | V-0 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Bending stress | | ISO178 | 93.0 Mpa |
| Tensile modulus | | ISO527-2 | 2300 Mpa |
| Tensile stress | | ISO527-2 | 62.0 Mpa |
| Tensile strain | | ISO527-2 | 6.5 % |
| Nominal tensile fracture strain | | ISO527-2 | 120 % |
| Flexural modulus | | ISO178 | 2500 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO179 | NoBreak |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC60093 | 6E+15 ohms |
| Volume resistivity | | IEC60093 | 3E+16 ohms·cm |
| dielectric strength | | IEC60243-1 | 31 KV/mm |
| dielectric strength | | IEC60243-1 | 18 KV/mm |
| | IEC60250 | 3.10 |
| | IEC60250 | 3.10 |
| Dissipation Factor | | IEC60250 | 6E-04 |
| Dissipation Factor | | IEC60250 | 9E-03 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO75-2/B | 140 °C |
| | ISO75-2/A | 126 °C |
| | ISO11359-2 | 6.5E-05 cm/cm/°C |
| | ISO11359-2 | 6.6E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.