Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792 | 1.20 g/cm³ |
| Water absorption rate | | ASTM D570 | 0.15 % |
| Water absorption rate | | ASTM D570 | 0.32 % |
| melt mass-flow rate | | ASTM D1238 | 10 g/10min |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ASTM D785 | 73 M（Scale） |
| Rockwell hardness | | ASTM D785 | 118 R |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| refractive index | | ASTM542 | 1.59 |
| transmittance | | ASTM D1003 | 89.0 ％ |
| Haze ratio | | ASTM D1003 | 1.1 ％ |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ASTM D638 | 60.0 MPa |
| elongation at break | | ASTM D638 | 150 % |
| Tensile modulus | | ASTM D638 | 2410 MPa |
| bending strength | | ASTM D790 | 96.0 MPa |
| Flexural modulus | | ASTM D790 | 2410 MPa |
| Impact strength of cantilever beam gap | | ASTM D256 | 900 J/m |
| Flame retardant performance | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL -94 | V-2 1.50mm |
| UL flame retardant rating | | UL -94 | V-0 3.00mm |
| UL flame retardant rating | | UL -94 | 0.75mm |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | ASTM D257 | 2E+17 Ω.cm |
| dielectric strength | | ASTM D149 | 17 KV/mm |
| dielectric strength | | ASTM D3638 | 250 V |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| vicat | | ASTM1525 | 146 °C |
| Linear coefficient of thermal expansion | | ASTM D696 | 6.8E-05 cm/cm／°C |
| Heat distortion temperature | | ASTM D648 | 138 °C |
| Heat distortion temperature | | ASTM D648 | 126 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.