PP Homopolymer ADDILENE H 210 G20 ADDIPLAST FRANCE

Properties:

Filler glass beads 20% filler by weight

Typical Applications:

Automotive internal components applications in the automotive field

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Automotive internal components \| applications in the automotive field
Properties:	Filler \| glass beads \| 20% \| filler by weight

Certificates

No Data...

Technical Data Sheet

mechanical properties	Test Condition	Test Method	Test Result	Test Unit
tensile strength	Break，23°C	ISO 527-2	24.0	MPa
Elongation at Break	Yield，23°C	ISO 527-2	>=100	%
Charpy Notched Impact Strength	23°C	ISO 179/1eA	3.0	kJ/m²
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	37.0	kJ/m²
Impact strength of cantilever beam gap	23°C	ISO 180/1A	3.0	kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	弹性模量	ISO 178	1550	MPa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	1.80MPaAnnealed	ISO 75-2/Af	62.0	°C
Vicat softening temperature		ISO 306/A50	153	°C
Vicat softening temperature	Vicat softening temperature	Melting Temperature	ISO 3146/C2	165-168	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
density		ISO 1183	1.01	g/cm³
melt mass-flow rate	℃/Kg	ISO 1133	3.0	g/10min
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Volume resistivity		IEC 60093	>=1.0E+14	Ω.cm
Surface resistivity		IEC 60093	1E+14	Ω.cm
Dissipation factor	相对漏电起痕指数	IEC 60112	>=600	V
hardness	Test Condition	Test Method	Test Result	Test Unit
Hardness (Shore A)		ISO 868	76

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.