Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO1183 | 1.17 g/cm³ |
| melt mass-flow rate | | ISO1133 | 1.7 g/10min |
| melt mass-flow rate | | ISO1133 | 3.4 g/10min |
| melt mass-flow rate | | ISO1133 | 5.9 g/10min |
| melt mass-flow rate | | ISO1133 | 9.2 g/10min |
| EthyleneContent | | 内部方法 | 38.0 mol% |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ISO2039-2 | 85 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO527-2 | 2400 MPa |
| Tensile stress | Break | ISO527-2 | 27.0 MPa |
| Tensile strain | Break | ISO527-2 | 15 % |
| Flexural modulus | | ISO178 | 4800 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO179 | 2.0 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO179 | 2.0 kJ/m² |
| film | Test Condition | Test Method | Test Result |
|---|
| oxygen permeability | | ISO14663-2 | 0.012 cm³·mm/m²/atm/24hr |
| oxygen permeability | | ISO14663-2 | 0.012 cm³·mm/m²/atm/24hr |
| oxygen permeability | | ISO14663-2 | 0.014 cm³·mm/m²/atm/24hr |
| oxygen permeability | | ISO14663-2 | 0.044 cm³·mm/m²/atm/24hr |
| oxygen permeability | | ISO14663-2 | 0.070 cm³·mm/m²/atm/24hr |
| Water vapor permeability | | ASTME96 | 0.96 g·mm/m²/atm/24hr |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Glass Transition Temperature | | ISO11357-2 | 53.0 °C |
| Crystallization peak temperature | | ISO11357-3 | 148 °C |
| vicat | | ISO306 | 158 °C |
| melting temperature | | ISO11357-3 | 172 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.