Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183 | 1.37 g/cm³ |
| Shrinkage rate 3 | | 内部方法 | 0.60 到 0.90 % |
| Shrinkage rate 3 | | 内部方法 | 0.20 到 0.50 % |
| Water absorption rate | | ISO 62 | 0.60 % |
| Water absorption rate | | ISO 62 | 5.5 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ISO 2039-2 | 97 |
| Rockwell hardness | | ISO 2039-2 | 24 |
| Rockwell hardness | | ISO 2039-2 | 121 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile stress | | ISO 527-2 | 235 Mpa |
| Tensile stress | | ISO 527-2 | 190 Mpa |
| Tensile stress | | ISO 527-2 | 120 Mpa |
| Tensile strain | | ISO 527-2 | 2.0 % |
| Tensile strain | | ISO 527-2 | 2.5 % |
| Tensile strain | | ISO 527-2 | 5.0 % |
| Flexural modulus | | ISO 178 | 11600 Mpa |
| Flexural modulus | | ISO 178 | 9500 Mpa |
| Flexural modulus | | ISO 178 | 5800 Mpa |
| Bending stress | | ISO 178 | 325 Mpa |
| Bending stress | | ISO 178 | 290 Mpa |
| Bending stress | | ISO 178 | 190 Mpa |
| compression stress | | ISO 604 | 250 Mpa |
| compression stress | | ISO 604 | 180 Mpa |
| compression stress | | ISO 604 | 110 Mpa |
| shear strength | | ASTM D732 | 95.0 Mpa |
| | ISO 9352 | 0.400 mg |
| Friction coefficient - vs. Metal 4 | | Suzuki Method | 0.15 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO 179 | 10 kJ/m² |
| Charpy Notched Impact Strength | | ISO 179 | 13 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO 179 | 60 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO 179 | 65 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | IEC 60093 | 1.0E+13 ohms·cm |
| dielectric strength | | IEC 60243-1 | 20 KV/mm |
| dielectric constant | | IEC 60250 | 4.60 |
| dielectric constant | | IEC 60250 | 4.40 |
| dielectric constant | | IEC 60250 | 3.90 |
| Dissipation Factor | | IEC 60250 | 0.020 |
| Dissipation Factor | | IEC 60250 | 0.020 |
| Dissipation Factor | | IEC 60250 | 0.020 |
| | UL 746 | 114 sec |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO 75-2/B | 262 °C |
| melting temperature | | DSC | 265 °C |
| | ISO 11359-2 | 2.0E-5 到 3.0E-5 cm/cm/°C |
| specific heat | | | 1800 J/kg/°C |
| thermal conductivity | | | 0.40 W/m/K |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.