Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183 | 1.08 g/cm3 |
| Water absorption rate | | ISO 62 | 0.09 % |
| processability | Test Condition | Test Method | Test Result |
|---|
| spiral flow length | | | -- cm |
| Shrinkage rate | | ISO 294-4 | 0.5-0.7 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ISO 527 | 50 MPa |
| elongation | Break | ISO 527 | 10 % |
| bending strength | | ISO 178 | 70 MPa |
| Flexural modulus | | ISO 178 | 2.28×103 MPa |
| Charpy Notched Impact Strength | Notched | ISO 179（leA） | 15 KJ/m2 |
| Flame retardant performance | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | V-1（1.5mm） |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Dielectric loss | | IEC 60250 | 3×10-3 |
| Volume resistivity | | IEC 60093 | 1×1014 Ω•m |
| dielectric strength | | IEC 60243 | 29 KV/m |
| arc resistance | | IEC 61621 | - Sec |
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | V |
| ash content | | | 0 % |
| dielectric constant | | IEC 60250 | 2.7 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Hot deformation temperature (HDT) | | ISO 75f | 90 ℃ |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare