Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Water absorption rate | Saturation | ISO 622 | 0.030 % |
| Water absorption rate | Equilibrium | ISO 622 | 0.23 % |
| density | | ISO 1183/A | 1.20 g/cm³ |
| density | | ISO 11832 | 1200 kg/m³ |
| melt mass-flow rate | | ISO 1133 | 15 g/10min |
| Melt volume flow rate | | ISO 11332 | 12.0 cm³/10min |
| Shrinkage rate | | ISO 294-4 | 0.50to0.70 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | V-2 |
| UL flame retardant rating | | UL 94 | V-0 |
| Burning Behav. | | ISO 12102 | V-2 |
| Burning Behav.atthicknessh | | ISO 12102 | V-0 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO 527-2/50 | 2300 MPa |
| Tensile modulus | | ISO 527-22 | 2300 MPa |
| tensile strength | Yield | ISO 527-2/50 | 60.0 MPa |
| tensile strength | Yield | ISO 527-22 | 60.0 MPa |
| tensile strength | Break | ISO 527-2/50 | 66.0 MPa |
| Tensile strain | Yield | ISO 527-2/50 | 6.0 % |
| Tensile strain | Yield | ISO 527-22 | 6.0 % |
| Tensile strain | Break | ISO 527-2/50 | 120 % |
| Nominal fracture strain | | ISO 527-22 | >50 % |
| Flexural modulus | | ISO 178 | 2400 MPa |
| bending strength | | ISO 178 | 100 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO 179/1eA | 20 kJ/m² |
| Charpy Notched Impact Strength | | ISO 179/1eA2 | 17.0 kJ/m² |
| Charpy Notched Impact Strength | | ISO 179/1eA2 | 15.0 kJ/m² |
| Charpy Notched Impact Strength | | ISO 179/1eU2 | NoBreak |
| Charpy Notched Impact Strength | | ISO 179/1eU2 | NoBreak |
| Impact strength of cantilever beam gap | | ISO 180/A | 83 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 2 |
| Compared to the Leakage Tracking Index (CTI) | | IEC 601122 | PLC 2 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO 75-2/A | 122 °C |
| Heat distortion temperature | | ISO 75-2/A | 139 °C |
| Heat distortion temperature | | ISO 75-22 | 122 °C |
| vicat | | ISO 306/B50 | 147 °C |
| vicat | | ISO 3062 | 147 °C |
| Ball pressure temperature | | IEC 60335-1 | 125 °C |
| Heat distortion temperature | | ISO 75-2/B | 142 °C |
| Heat distortion temperature | | ISO 75-22 | 140 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.