Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| melt viscosity | | ISO11443 | 220 Pa·s |
| density | | ISO1183 | 1.38 g/cm³ |
| Shrinkage rate | | ISO294-4 | 0.70to1.3 % |
| Shrinkage rate | | ISO294-4 | 0.10to0.40 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO527-2 | 6000 MPa |
| Tensile stress | | ISO527-2 | 100 MPa |
| Tensile strain | | ISO527-2 | 2.8 % |
| Flexural modulus | | ISO178 | 5300 MPa |
| Bending stress | | ISO178 | 150 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO179/1eA | 7.5 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | IEC60093 | 1E+14 ohms·cm |
| dielectric strength | | IEC60243-1 | 20 kV/mm |
| Surface Resistivity | | IEC60093 | 1E+13 ohms |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| melting temperature | | ISO11357-3 | 225 °C |
| | ISO75-2/A | 160 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare