Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO1183 | 1.10 g/cm³ |
| SpiralFlow | | 内部方法 | 85.0 cm |
| Shrinkage rate | | ISO294-4 | 1.7 % |
| Shrinkage rate | | ISO294-4 | 1.3 % |
| Humidity Absorption | | ISO1110 | 2.6 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| | ISO2039-1 | 102 MPa |
| flammability | Test Condition | Test Method | Test Result |
|---|
| burning rate | | FMVSS302 | <100 mm/min |
| FlameRating | | UL94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO527-2/1 | 2700 MPa |
| Flexural modulus | | ISO178 | 2600 MPa |
| Tensile stress | Yield | ISO527-2/50 | 70.0 MPa |
| Tensile strain | Yield | ISO527-2/50 | 4.3 % |
| Tensile strain | Break | ISO527-2/50 | >45 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO179/1eA | 8.0 kJ/m² |
| Charpy Notched Impact Strength | | ISO179/1eA | 10 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO179/1eU | NoBreak |
| Impact strength of simply supported beam without notch | | ISO179/1eU | NoBreak |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO75-2/B | 162 °C |
| | ISO75-2/A | 60.0 °C |
| melting temperature | | DINEN11357-1 | 222 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.