Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792 | 1.20 g/cm³ |
| melt mass-flow rate | | ASTM D1238 | 8.0 g/10min |
| Water absorption rate | Equilibrium | ASTM D570 | 1.2 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | Shore A | ASTM D2240 | 80 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ASTM D638 | 6.96 MPa |
| Tensile modulus | | ASTM D638 | 7.24 MPa |
| tensile strength | | ASTM D638 | 41.4 MPa |
| elongation | | ASTM D638 | 450 % |
| Flexural modulus | | ASTM D790 | 37.9 MPa |
| bending strength | | ASTM D790 | 2.41 MPa |
| coefficient of friction | Itself - Dynamic | ASTM D1894 | 1.5 |
| elastomer | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ASTM D412 | 5.34 MPa |
| tensile strength | | ASTM D412 | 4.14 MPa |
| tensile strength | Yield | ASTM D412 | 45.5 MPa |
| elongation | Yield | ASTM D412 | 480 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| dielectric strength | | ASTM D149 | 14 kV/mm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| vicat | | ASTM D1525 | 71.1 °C |
| melting temperature | | | 191to221 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.