Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| melt mass-flow rate | | ASTM D1238 | 22 g/10 min |
| Shrinkage rate | | ASTM D955 | 0.60 - 0.65 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | V-0 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ASTM D638 | 53.0 Mpa |
| Flexural modulus | | ASTM D790 | 2280 Mpa |
| bending strength | | ASTM D790 | 82.4 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Suspended wall beam without notch impact strength | | ASTM D256 | 590 J/m |
| injection | Test Condition | Test Method | Test Result |
|---|
| drying temperature | | | 100 to 110 °C |
| drying time | | | 3.0 to 5.0 hr |
| Temperature at the rear of the barrel | | | 270 to 290 °C |
| Temperature in the middle of the barrel | | | 280 to 300 °C |
| Temperature at the front of the material cylinder | | | 285 to 305 °C |
| Spray nozzle temperature | | | 295 to 315 °C |
| Temperature | | | 50 to 80 °C |
| Back pressure | | | 0.490 to 2.94 Mpa |
| screw speed | | | 30 to 50 rpm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D648 | 122 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.