PPS 1131L4 CELANESE USA

Form：Granules | Grade：Enhanced level

Properties:

Glass fiber reinforcedHigh temperature resistan

Typical Applications:

Automotive ApplicationsElectrical applications

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Automotive Applications \| Electrical applications
Properties:	Glass fiber reinforced \| High temperature resistan

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	42	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	42	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	0.38 mm	UL 94	V-0
UL flame retardant rating	UL flame retardant rating	1.5 mm	UL 94	V-0
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus		ISO 527-2/1A	12200	Mpa
tensile strength	Break	ISO 527-2/1A/5	165	Mpa
Tensile strain	Break	ISO 527-2/1A/5	1.9	%
Bending modulus	23°C	ISO 178	12000	Mpa
bending strength		ISO 178	255	Mpa
injection	Test Condition	Test Method	Test Result	Test Unit
drying temperature			100 to 110	°C
drying time			3.0 to 4.0	hr
Suggested maximum moisture content			0.020	%
Hopper temperature			20 to 30	°C
Temperature at the rear of the barrel			290 to 300	°C
Temperature in the middle of the barrel			310 to 320	°C
Temperature at the front of the material cylinder			330 to 340	°C
Spray nozzle temperature			310 to 330	°C
Processing (melt) temperature			330 to 340	°C
Mold temperature			140 to 160	°C
Injection speed			快速
Back pressure			< 3.00	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	1.8 MPa, Unannealed	ISO 75-2/A	265	°C
Hot deformation temperature	Hot deformation temperature	8.0 MPa, Unannealed	ISO 75-2/C	205	°C
Glass transition temperature		ISO 11357-2	90.0	°C
Melting temperature		ISO 11357-3	280	°C
Linear coefficient of thermal expansion	Flow	ISO 11359-2	2.9E-5	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Across Flow	ISO 11359-2	6.2E-5	cm/cm/°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Shrinkage rate	横向Flow	ISO 294-4	0.50 - 0.80	%
Shrinkage rate	Shrinkage rate	Flow	ISO 294-4	0.30 - 0.70	%
Water absorption rate	Saturation, 23°C	ISO 62	0.020	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Surface resistivity		IEC 60093	> 1.0E+15	ohms
Volume resistivity		IEC 60093	> 1.0E+15	ohms·cm
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	M -Sale	ISO 2039-2	100

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.