POM HOSTAFORM® C27021 GV3/30 BK
28
- Properties:Chemical resistanceantioxidantHydrolysis resistance
- Usages:Bottle capElectrical applications
Compare
View PricesTechnical Data Sheet
| Basic performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ISO 1183 | 1.41 g/cm³ | |
| Water absorption rate | ISO 62 | 0.20 % | |
| ISO 62 | 0.70 % | ||
| melt mass-flow rate | ISO 1133 | 34.55 g/10min |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy without notch impact strength | ISO 179 1eU | 12.0 J/cm² | |
| Charpy notch impact strength | ISO 179 1eA | 0.550 J/cm² | |
| Tensile creep modulus | ISO 899 part 1 | 2400 Mpa | |
| ISO 899 part 1 | 1300 Mpa | ||
| ball indentation hardness | ISO 2039 part 1 | 147 Mpa | |
| Yield tensile strength | ISO 527 part 1/2 | 63.0 Mpa | |
| elongation at break | ISO 527 part 1/2 | 17.0 % | |
| elongation | ISO 527 part 1/2 | 8.0 % | |
| Tensile modulus | ISO 527 part 1/2 | 2800 Mpa | |
| Flexural modulus | ISO 178 | 2700 Mpa | |
| Charpy without notch impact strength | ISO 179 1eU | 12.0 J/cm² | |
| Charpy notch impact strength | ISO 179 1eA | 0.550 J/cm² |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ISO 11359 part 1/2 | 110 µm/m-℃ | ||
| melting point | ISO 3146 method C1b | 166 °C | |
| ISO 75 part 1/2 | 100 °C | ||
| vicat | ISO 306 | 150 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.