PA66

PA66 BESTNYL SE30VI02AS08 TRIESA SPAIN

Compare

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch	23°C	ISO 179	72 kJ/m²
Charpy Notched Impact Strength	23°C	ISO 179	7.5 kJ/m²

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating		UL 94	HB
Burning rate		FMVSS302	<100 mm/min

mechanical properties	Test Condition	Test Method	Test Result
Tensile strain	Break	ISO 527-2	3.0 %
tensile strength		ISO 527-2	172 MPa
Tensile modulus		ISO 527-2	9400 MPa

thermal performance	Test Condition	Test Method	Test Result
Vicat softening temperature		ISO 306	>260 °C
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	250 °C

Physical properties	Test Condition	Test Method	Test Result
ash content		Internal Method	30 %
humidity	颗粒	ISO 1110	0.20 %
Water absorption rate	23°C,24hr	ISO 62	0.80 %
Shrinkage rate		ISO 294-4	0.50 %
density		ISO 1183	1.38 g/cm³

Electrical performance	Test Condition	Test Method	Test Result
Dielectric strength		IEC 60243-1	32 kV/mm
Surface resistivity		IEC 60093	1E+15 ohms

hardness	Test Condition	Test Method	Test Result
Shore hardness	ShoreD	ISO 868	81

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.