PP Piolen® P B50A19 PiO Kunststoffe GmbH & Co KG

Properties:
Filler barium sulfate 50% filler by weight
Usages:
Applications in the automotive industry parts under the hood of automobiles
Compare

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength	-40°C	ISO 179/1eA	1.5 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA	3.7 kJ/m²
Impact strength of simply supported beam without notch	-40°C	ISO 179/1eU	6.7 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	14 kJ/m²

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating		UL 94	HB

mechanical properties	Test Condition	Test Method	Test Result
tensile strength	Break	ISO 527-2	19.0 MPa
Tensile strain	Break	ISO 527-2	56 %
Bending modulus		ISO 178	2100 MPa
tensile strength	Yield	ISO 527-2	22.0 MPa

thermal performance	Test Condition	Test Method	Test Result
Crystallization peak temperature	DSC	ISO 3146	160to170 °C
Vicat softening temperature	--	ISO 306/A	151 °C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B	89.0 °C

Physical properties	Test Condition	Test Method	Test Result
density		ISO 1183	1.51 g/cm³
melt mass-flow rate	230°C/2.16kg	ISO 1133	20 g/10min

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.