PA6 J-1/30/TF/15 DSM HOLAND

Form：Granules | Grade：Enhanced level

Properties:

Filler: Glass fiber reinf30% filler by weight

Typical Applications:

CamPulleybearingEngine parts

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Cam \| Pulley \| bearing \| Engine parts
Properties:	Filler: Glass fiber reinf \| 30% filler by weight

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Charpy Notched Impact Strength	23°C	ISO 179/1eA2	10.0	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	1.6mm	UL 94	HB
Normal combustion performance with a thickness of 1.6mm	1.50mm,UL		HB	4.21
Burning Behav.atthicknessh	1.50mm,UL		HB	4.21
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus		ISO 527-22	9000	Mpa
tensile strength		ASTM D638	159	Mpa
tensile strength	tensile strength	Break	ISO 527-22	160	Mpa
elongation	Break	ASTM D638	2.5	%
Tensile strain	Break	ISO 527-22	2.5	%
Bending modulus	23°C	ASTM D790	9310	Mpa
bending strength		ASTM D790	238	Mpa
bending strength	bending strength	Break,23°C	ASTM D790	238	Mpa
compressive strength		ASTM D695	193	Mpa
shear strength		ASTM D732	68.9	Mpa
Friction coefficient	Steel - Dynamic	ASTM D1894	0.25
Friction coefficient	Friction coefficient	Steel - Static6	ASTM D1894	0.20
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	1.8MPa	ISO 75-22	250	°C
Melting temperature		ISO 11357-32	260	°C
Linear coefficient of thermal expansion	MD	ASTM D696	4.3E-05	cm/cm/°C
RTI Elec	1.5mm	UL 746	65.0	°C
RTI Imp	1.5mm	UL 746	65.0	°C
RTI Str	1.5mm	UL 746	65.0	°C
Hot deformation temperature	0.45MPa,Unannealed	ASTM D648	260	°C
	Hot deformation temperature	0.45MPa	ISO 75-22	260	°C
	Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ASTM D648	254	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	Equilibrium	ISO 622	1.4	%
Shrinkage rate	MD：3.18mm	ASTM D955	0.20	%
Water absorption rate	24hr	ASTM D570	0.60	%
Water absorption rate	Water absorption rate	Saturation	ISO 622	5.3	%
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	R-Scale	ASTM D785	119

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.