PA6 SCHULAMID® 6 NV 12 FR A SCHULMAN USA

Product Description

Certificates(0)

Datasheet

Product Description

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	3.5	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA	4.0	kJ/m²
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	NoBreak
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	NoBreak
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	1.5mm	UL 94	V-0
	UL flame retardant rating	0.75mm	UL 94	V-0
	UL flame retardant rating	UL flame retardant rating	0.38mm	UL 94	V-0
Hot filament ignition temperature	3.0mm	IEC 60695-2-13	750	°C
	Hot filament ignition temperature	1.5mm	IEC 60695-2-13	750	°C
	Hot filament ignition temperature	Hot filament ignition temperature	0.38mm	IEC 60695-2-13	750	°C
Burning wire flammability index	3.0mm	IEC 60695-2-12	960	°C
Burning rate	0.750mm,Self-Extinguishing	ISO 3795	0.0	mm/min
	Burning rate	1.50mm,自动灭火	ISO 3795	0.0	mm/min
	Burning rate	Burning rate	3.00mm,自动灭火	ISO 3795	0.0	mm/min
UL flame retardant rating	0.75mm	IEC 60695-11-10,-20	V-0
	UL flame retardant rating	1.5mm	IEC 60695-11-10,-20	V-0
	UL flame retardant rating	UL flame retardant rating	3.0mm	IEC 60695-11-10,-20	V-0
Burning wire flammability index	0.38mm	IEC 60695-2-12	960	°C
	Burning wire flammability index	0.75mm	IEC 60695-2-12	960	°C
	Burning wire flammability index	Burning wire flammability index	1.5mm	IEC 60695-2-12	960	°C
UL flame retardant rating	3.0mm	UL 94	V-0
UL flame retardant rating	UL flame retardant rating	0.38mm	IEC 60695-11-10,-20	V-0
Extreme Oxygen Index		ISO 4589-2	36	%
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile strain	Yield	ISO 527-2/1A/50	4.0	%
tensile strength	Yield	ISO 527-2/1A/50	70.0	MPa
Tensile modulus		ISO 527-2/1A/1	4200	MPa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
RTI Str	3.0mm	UL 746	95.0	°C
RTI Elec	3.0mm	UL 746	130	°C
	RTI Elec	1.5mm	UL 746	130	°C
	RTI Elec	RTI Elec	0.75mm	UL 746	130	°C
Ball Pressure Test	200°C	IEC 60695-10-2	Pass
Vicat softening temperature	--	ISO 306/B50	203	°C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/A50	218	°C
RTI Imp	3.0mm	UL 746	80.0	°C
	RTI Imp	1.5mm	UL 746	75.0	°C
	RTI Imp	RTI Imp	0.75mm	UL 746	75.0	°C
RTI Str	1.5mm	UL 746	95.0	°C
RTI Str	RTI Str	0.75mm	UL 746	95.0	°C
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/Bf	200	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/Af	90.0	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Stickiness		ISO 307	130	cm³/g
density		ISO 1183/A	1.15	g/cm³
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Surface resistivity		IEC 60093	>1.0E+15	ohms
Volume resistivity		IEC 60093	>1.0E+13	ohms·cm
Compared to the anti leakage trace index		IEC 60112	PLC 0
High arc combustion index	0.75mm	UL 746	PLC 3
	High arc combustion index	1.5mm	UL 746	PLC 3
	High arc combustion index	High arc combustion index	3.0mm	UL 746	PLC 2
Hot wire ignition	19.1mm	UL 746	PLC 0
	Hot wire ignition	38.1mm	UL 746	PLC 0
	Hot wire ignition	Hot wire ignition	76.2mm	UL 746	PLC 0

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.