LLDPE FP120-A NOVA CANADA

Form：Granules | Grade：Injection grade

Properties:

high strengthHigh toughnessEasy to processHigh rigidity

Typical Applications:

chipPlatePackaging film

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	chip \| Plate \| Packaging film
Properties:	high strength \| High toughness \| Easy to process \| High rigidity

Certificates

No Data...

Technical Data Sheet

optical performance	Test Condition	Test Method	Test Result	Test Unit
gloss	45°,25.0μm,Blown Film	ASTM D2457	59
turbidity	25.0μm,Blown Film	ASTM D1003	10	%
Physical properties	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate	190°C/2.16kg	ASTM D1238	1.0	g/10min
film	Test Condition	Test Method	Test Result	Test Unit
film thickness			25	µm
Secant modulus	1%Secant,MD:25μm,Blown Film	ASTM D882	175	Mpa
Secant modulus	Secant modulus	1%Secant,TD:25μm,Blown Film	ASTM D882	195	Mpa
tensile strength	MD:Yield,25μm,Blown Film	ASTM D882	10.0	Mpa
	tensile strength	TD:Yield,25μm,Blown Film	ASTM D882	10.0	Mpa
		tensile strength	MD:Break,25μm,Blown Film	ASTM D882	48.0	Mpa
		tensile strength	tensile strength	TD:Break,25μm,Blown Film	ASTM D882	32.0	Mpa
elongation	MD:Break,25μm,Blown Film	ASTM D882	480	%
elongation	elongation	TD:Break,25μm,Blown Film	ASTM D882	670	%
Dart impact	25μm,Blown Film	ASTM D1709A	270	g
Elmendorf tear strength	MD:25μm,Blown Film	ASTM D1922	420	g
Elmendorf tear strength	Elmendorf tear strength	TD:25μm,Blown Film	ASTM D1922	610	g
Supplementary Information	Test Condition	Test Method	Test Result	Test Unit
Low friction puncture	25.0μm，吹膜	Internal Method	360	J/cm

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.