- Properties:Mechanical properties
CompareTechnical Data Sheet
| Test Condition | Test Method | Test Result | |
|---|---|---|---|
| yield | % | 290to460 | |
| Volume resistivity | 2.75to3.40 | ||
| yield | 8.0to42.76 Mpa | ||
| fracture | 4.0to20.83 Mpa | ||
| elongation | Break | % | 100to120 |
| Water Vapor Transmission Rate | g/100 | 0.17to0.25 | |
| tensile strength | Yield | 49.66to60.83 Mpa | |
| brittle temperature | °C | -50--4 | |
| melting temperature | °C | 158to185 | |
| burning rate | mm/min | 4.318to6.35 | |
| tensile strength | 7.86to23.59 Mpa | ||
| melt mass-flow rate | g/10min | 6.2to7.0 | |
| Shrinkage rate | mm/mm | 101.6E-3-1.016 | |
| K-Value | 56.5to80.3 | ||
| Viscosity value | ml/g | 83.1to161.4 | |
| dielectric strength | V/mil | 340to1000 | |
| elongation | % | 220to390 | |
| compression set | % | 47to48 | |
| yield | 55.38to94.48 Mpa | ||
| fracture | % | 200to410 | |
| % | 180to470 | ||
| Continuous use temperature | °C | 59to105 | |
| Linear coefficient of thermal expansion | mm/mm/°C | 88.9E-5到101.6E-5 | |
| Impact strength of simply supported beam without notch | kJ/m² | 2.414to5.572 | |
| Suspended wall beam without notch impact strength | kJ/m² | 2.414to4.643 | |
| Dart impact | N.m/mil | 12.57to53.10 | |
| Impact strength of cantilever beam gap | kJ/m² | 1.582to14.532 | |
| fracture | 5.52to32.14 Mpa | ||
| yield | 32.97to62.0 Mpa | ||
| Shore hardness | 12to108 | ||
| 48to97 | |||
| Haze ratio | % | 1.5to3.0 | |
| transmissivity | % | 88.8to90.1 | |
| Apparent density | 1.16to1.50 | ||
| Water absorption rate | % | 0.020to0.16 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.