PC/ABS CY5005-WH9G286 SABIC INNOVATIVE NANSHA

Form：Granules

Properties:

High temperature resistanHigh mobility

Typical Applications:

Electrical applicationsHome appliance components

Supplier(0)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Electrical applications \| Home appliance components
Properties:	High temperature resistan \| High mobility

Certificates

No Data...

Technical Data Sheet

UL	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	1.5mm	UL 94	V-1
UL flame retardant rating	UL flame retardant rating	2.022mm	UL 94	V-0
RTI Elec	全色 1.5mm	UL 746B	60	°C
RTI Elec	RTI Elec	全色 2.0~2.2mm	UL 746B	60	°C
RTI Imp	全色 1.5mm	UL 746B	60	°C
RTI Imp	RTI Imp	全色 2.0~2.2mm	UL 746B	60	°C
RTI Str	全色 1.5mm	UL 746B	60	°C
RTI Str	RTI Str	全色 2.0~2.2mm	UL 746B	60	°C
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus	23℃	ASTM D638	2800	Mpa
Tensile modulus	Tensile modulus	23℃	ISO 527	2670	Mpa
tensile strength	23℃ 50mm/min	ASTM D638	48	Mpa
	tensile strength	Yield23℃	ASTM D638	65	Mpa
	tensile strength	tensile strength	23℃ 50mm/min	ISO 527	43	Mpa
Stretching degree	Yield23℃	ISO 527	63	Mpa
Stretching degree	Stretching degree	1.0kg	ASTM D638	34	%
elongation	Yield23℃ 50mm/min	ASTM D638	3.9	%
	elongation	23℃	ISO 527	40	%
	elongation	elongation	Yield23℃ 50mm/min	ISO 527	3.5	%
bending strength	Yield23℃	ASTM D790	97	Mpa
bending strength	bending strength	Yield23℃	ISO 178	95	Mpa
Bending modulus	23℃	ASTM D790	2630	Mpa
Bending modulus	Bending modulus	23℃	ISO 178	2700	Mpa
Impact strength of cantilever beam gap	23℃	ASTM D256	90	J/m
	Impact strength of cantilever beam gap	-30℃	ASTM D256	69	J/m
		Impact strength of cantilever beam gap	23℃	ISO 180	10	kJ/m²
		Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	-30℃	ISO 180	5	kJ/m²
Charpy Notched Impact Strength	23℃	ISO 179	10	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	-30℃	ISO 179	5	kJ/m²
Dart impact			20
Hot deformation temperature	Unannealed1.8MPa	ASTM D648	81	°C
Hot deformation temperature	Hot deformation temperature	Unannealed1.8MPa	ISO 75	73	°C
Vicat softening temperature	50℃/hr 50N	ISO 306	89	°C
Vicat softening temperature	Vicat softening temperature	120℃/hr 50N	ISO 306	92	°C
Linear coefficient of thermal expansion	Flow	ISO 11359	0.000075	cm/cm/℃
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Across Flow	ISO 11359	0.000075	cm/cm/℃
Physical properties	Test Condition	Test Method	Test Result	Test Unit
density		ASTM D792	1.18	g/cm³
density	density		ISO 1183	1.18	g/cm³
Shrinkage rate	Flow3.2mm	ASTM D995	0.4	%
Shrinkage rate	Shrinkage rate	垂直3.2mm	ASTM D995	0.6	%
Water absorption rate	23℃Saturation	ISO 62	0.1	%
Water absorption rate	Water absorption rate	23℃50RH	ISO 62	0.05	%
melt mass-flow rate	260℃ 2.16kg	ASTM D1238	31	g/10min
melt mass-flow rate	melt mass-flow rate	260℃ 2.16kg	ISO 1133	27	g/10min
flame retardant performance	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	2.0-2.2mm	UL 94	\A0

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.