| physical property | Test Condition | Test Method | Test Result |
|---|
| melt mass-flow rate | | ASTM D1238 | 17 g/10min |
| Shrinkage rate | | ASTM D955 | 0.60 % |
| Water absorption rate | | ASTM D570 | 0.15 % |
| density | | ASTM D792 | 1.09 g/cm³ |
| melt mass-flow rate | | ASTM D1238 | 7.0 g/10min |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | R-Scale | ASTM D785 | 113 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| Hot filament ignition temperature | | AS/NZS60695.2.12 | 550 °C |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ASTM D638 | 51.0 MPa |
| elongation | | ASTM D638 | 100 % |
| Flexural modulus | | ASTM D790 | 2450 MPa |
| bending strength | | ASTM D790 | 88.0 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256 | 500 J/m |
| Dart impact | | ASTM D3029 | 45.0 J |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D648 | 106 °C |
| vicat | | ASTM D15254 | 125 °C |
| Linear coefficient of thermal expansion | | ASTM D696 | 7E-05 cm/cm/°C |
| Heat distortion temperature | | ASTM D648 | 96.0 °C |
| Heat distortion temperature | | ASTM D648 | 101 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.