PA66 AK-TF4315 Suzhou Walker
0
- Properties:30% fiberglass reinforced15% PTFE lubricatedhigh rigiditywear-resistant
CompareTechnical Data Sheet
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melting temperature | ISO 3146 | 260 ℃ |
| Test Condition | Test Method | Test Result | |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eU | 70 kJ/m2 | |
| Heat Deflection Temperature | 1.8 MPa | ISO 75 | 245 ℃ |
| vicat | ISO 306 | 240 ℃ | |
| filler content | 30 % | ||
| shrinkage rate | ASTM D955 | -- % | |
| Elongation at break | ISO 527 | 2.5 % | |
| tensile strength | ISO 527 | 150 MPa | |
| flexural modulus | ISO 178 | 8500 MPa | |
| bending strength | ISO 178 | 215 MPa |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ISO 1183 | 1.49 g/cm3 |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile modulus | ISO 527 | 9500 MPa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.