Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| melt mass-flow rate | | ISO1133 | 33 g/10min |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ISO2039-2 | 49 |
| Basic performance | Test Condition | Test Method | Test Result |
|---|
| melt mass-flow rate | | ISO 1133 | 33 g/10min |
| density | | ISO 1183 | 0.910 g/cm³ |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| elongation | | ISO 527 | 400 % |
| Flexural modulus | | ISO 527 | 700 Mpa |
| Impact Strength | | ISO 179 | 7.5 kJ/m² |
| Impact Strength | | ISO 179 | 2.5 kJ/m² |
| Rockwell hardness | | ISO 2039-2 | 49 R scale |
| tensile strength | | ISO 527 | 20.0 Mpa |
| Tensile modulus | | ISO527-2 | 700 Mpa |
| Tensile stress | | ISO527-2 | 20.0 Mpa |
| Tensile strain | | ISO527-2 | 400 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO179 | 2.5 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO179 | 7.5 kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO 75 | 65 °C |
| | ISO75-2/B | 65.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.