PA66 TECHNYL® A 218 V25 BK 21 N
68
- Properties:Glass fiber reinforcedFiller: Glass fiber reinf25% filler by weight
- Usages:Fitness equipmentAutomotive ApplicationsShellbearing
Compare
View PricesTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Shrinkage rate | 内部方法 | 0.85 % | |
| 内部方法 | 0.40 % | ||
| Water absorption rate | ISO 62 | 0.90 % | |
| Shrinkage rate | 内部方法 | 0.470 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1A | 8700 Mpa | |
| tensile strength | ISO 527-2/1A | 179 Mpa | |
| Tensile strain | ISO 527-2/1A | 3.0 % | |
| Flexural modulus | ISO 178 | 7600 Mpa | |
| bending strength | ISO 178 | 280 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of simply supported beam without notch | ISO 179/1eU | 65 kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 263 °C | |
| Linear coefficient of thermal expansion | ISO 11359-2 | 2.7E-05 cm/cm/°C | |
| Heat distortion temperature | ISO 75-2/Af | 255 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.