PBT/ABS NOVALLOY B B3708

159

Properties:
Low warpage
Glass fiber reinforced
enhance
Filler: Glass fiber reinf
40% filler by weight
Compare

Technical Data Sheet

physical property	Test Condition	Test Method	Test Result
Shrinkage rate		ASTM D955	0.20-0.40 %
Water absorption rate		ISO 62	0.15 %

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating		UL 94	HB

Mechanical properties	Test Method	Test Result
tensile strength	ISO 527-2	100 Mpa
Flexural modulus	ISO 178	11500 Mpa
bending strength	ISO 178	160 Mpa

Electrical performance	Test Condition	Test Method	Test Result
High arc combustion index (HAI)		UL 746	PLC 3
High Voltage Arc Traceability Rate (HVTR)		UL 746	mm/min
High Voltage Arc Traceability Rate (HVTR)	High Voltage Arc Traceability Rate (HVTR)		UL 746	PLC 1
Hot wire ignition (HWI)		UL 746	PLC 4 sec
Hot wire ignition (HWI)	Hot wire ignition (HWI)		UL 746	PLC 4
dielectric strength		ASTM D149	24 KV/mm
arc resistance		ASTM D495	124 sec
arc resistance	arc resistance		ASTM D495	PLC 5
Compared to the Leakage Tracking Index (CTI)		UL 746	PLC 1
Compared to the Leakage Tracking Index (CTI)	Compared to the Leakage Tracking Index (CTI)		IEC 60112	PLC 1
High arc combustion index (HAI)		UL 746	PLC 3

Thermal performance	Test Condition	Test Method	Test Result
Heat distortion temperature		ASTM D648	210 °C
	Heat distortion temperature		ISO 75-2/B	210 °C
		Heat distortion temperature		ASTM D648	200 °C
		Heat distortion temperature	Heat distortion temperature		ISO 75-2/A	190 °C
Linear coefficient of thermal expansion		ISO 11359-2	3E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion		ISO 11359-2	8E-05 cm/cm/°C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.