Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Specific volume | | ASTMD792 | 0.835 cm³/g |
| melt mass-flow rate | | ASTMD1238 | 2.0 g/10min |
| Melt volume flow rate | | ISO1133 | 2.00 cm³/10min |
| Shrinkage rate | | 内部方法 | 0.80到1.0 % |
| saturation | | ISO62 | 0.16 % |
| Balance, | | ISO62 | 0.35 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | M-Scale | ASTMD785 | 92 |
| Rockwell hardness | R-Scale | ASTMD785 | 127 |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| refractive index | | ASTMD542 | 1.600 |
| transmissivity | | ASTMD1003 | 85.0 % |
| Haze ratio | | ASTMD1003 | 1.0 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| yield | | ASTMD790 | 97.2 MPa |
| yield | | ASTMD638 | 65.5 MPa |
| yield | | ISO527-2/50 | 68.0 MPa |
| fracture | | ASTMD638 | 77.9 MPa |
| fracture | | ISO527-2/50 | 68.0 MPa |
| yield | | ASTMD638 | 8.0 % |
| yield | | ISO527-2/50 | 7.0 % |
| fracture | | ASTMD638 | 78 % |
| fracture | | ISO527-2/50 | 100 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Suspended wall beam without notch impact strength | | ASTMD4812 | 3200 J/m |
| Dart impact equipped with measuring instruments | | ASTMD3763 | 74.0 J |
| Falling hammer impact | | ASTMD3029 | 149 J |
| Tensile impact strength | | ASTMD1822 | 578 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | ASTMD257 | >2.5E+17 ohms·cm |
| dielectric strength | | ASTMD149 | 20 kV/mm |
| dielectric constant | | ASTMD150 | 3.27 |
| dielectric constant | | ASTMD150 | 3.27 |
| dielectric constant | | ASTMD150 | 3.10 |
| Dissipation Factor | | ASTMD150 | 1.6E-03 |
| Dissipation Factor | | ASTMD150 | 1.6E-03 |
| Dissipation Factor | | ASTMD150 | 0.026 |
| arc resistance | | ASTMD495 | PLC6 |
| Compared to the Leakage Tracking Index (CTI) | | UL746 | PLC 3 |
| High arc combustion index (HAI) | | UL746 | PLC 3 |
| High Voltage Arc Traceability Rate (HVTR) | | UL746 | PLC 3 |
| Hot wire ignition (HWI) | | UL746 | PLC 2 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| thermal conductivity | | ASTMC177 | 0.21 W/m/K |
| RTI Elec | | UL746 | 130 °C |
| RTI Imp | | UL746 | 130 °C |
| RTI | | UL746 | 130 °C |
| specific heat | | ASTMC351 | 1260 J/kg/°C |
| Flow:- | | ASTME831,ISO11359-2 | 6E-05 cm/cm/°C |
| Flow:- | | ASTME831 | 8.1E-05 cm/cm/°C |
| Horizontally:- | | ASTME831,ISO11359-2 | 6E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.