Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183 | 1.30 g/cm³ |
| Water absorption rate | | ISO 62 | 0.28 % |
| Water absorption rate | | ISO 62 | 0.090 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | V-0 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO 527-2/1 | 2600 MPa |
| tensile strength | | ISO 527-2/5 | 55.0 MPa |
| Tensile strain | | ISO 527-2/5 | 8.0 % |
| bending strength | | ISO 178 | 90.0 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO 179/1eA | 14 kJ/m² |
| Charpy Notched Impact Strength | | ISO 179/1eA | 18 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 无断裂 |
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 无断裂 |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 0 |
| relative permittivity | | IEC 60250 | 3.10 |
| Dissipation Factor | | IEC 60250 | 0.015 |
| Surface Resistivity | | IEC 60093 | >1.0E+15 ohms |
| Volume resistivity | | IEC 60093 | 1E+17 ohms·cm |
| dielectric strength | | IEC 60243-1 | 25 kV/mm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| melting temperature | | ISO 3146 | 223 °C |
| Linear coefficient of thermal expansion | | DIN 53752 | 9E-05 cm/cm/°C |
| Linear coefficient of thermal expansion | | DIN 53752 | 1E-04 cm/cm/°C |
| maximum service temperature | | IEC 216 | 11020000hrs °C |
| maximum service temperature | | IEC 216 | 130 °C |
| Heat distortion temperature | | ISO 75-2/B | 100 °C |
| Heat distortion temperature | | ISO 75-2/A | 80.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.