LDPE AT 520
10
- Properties:High mobilityBondable
- Usages:sealantadhesivefilm
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | ASTMD1238 | 2.0 g/10min | |
| ASTM D-1238 | 2.0 g/10min |
| optical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| gloss | ASTMD2457 | 54 | |
| Haze ratio | ASTMD1003 | 14 % | |
| gloss | ASTM D-2457 | 54 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile yield strength | 12 | ||
| tensile breaking strength | ASTM D-882 | 21 MPa | |
| 20 | |||
| 1% secant modulus | ASTM D-882 | 210 MPa | |
| 240 | |||
| elongation at break | ASTM D-882 | 400 % | |
| 600 |
| film | Test Condition | Test Method | Test Result |
|---|---|---|---|
| elongation | ASTMD882 | 600 % | |
| Falling hammer impact | ASTMD1709 | 100 g | |
| Film thickness - tested | 50 µm | ||
| Secant modulus | ASTMD882 | 210 Mpa | |
| ASTMD882 | 240 Mpa | ||
| tensile strength | ASTMD882 | 12.0 Mpa | |
| ASTMD882 | 12.0 Mpa | ||
| ASTMD882 | 21.0 Mpa | ||
| ASTMD882 | 20.0 Mpa | ||
| elongation | ASTMD882 | 400 % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.