ABS CU-301 DENKA JAPAN

Form：Granules | Grade：Impact resistant grade

Properties:

High impact resistancetransparent

Supplier(0)

Product Description

Certificates(0)

Datasheet

Product Description

Properties:

High impact resistance | transparent

Certificates

No Data...

Technical Data Sheet

machinability	Test Condition	Test Method	Test Result	Test Unit
Shrinkage rate	2mmt		0.3-0.5	%
Basic Performance	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate	220℃*10kg	JIS K-6874	18	g/10min
melt mass-flow rate	melt mass-flow rate	200℃*5kg	JIS K-6874	1.4	g/10min
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
tensile strength		ASTM D638/ISO 527	33	kg/cm²(MPa)[Lb/in²]
Rockwell hardness		ASTM D785	33
Bending modulus		ASTM D790/ISO 178	1770	kg/cm²(MPa)[Lb/in²]
bending strength		ASTM D790/ISO 178	61	kg/cm²(MPa)[Lb/in²]
Impact strength of cantilever beam gap		ASTM D256/ISO 179	180	kg·cm/cm(J/M)ft·lb/in
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	1/4＂带Notched	ASTM D-256	180	J/m
bending strength		ASTM D-790	61	Mpa
Rockwell hardness	M尺度	ASTM D-785	33
tensile strength		ASTM D-638	33	Mpa
Bending modulus		ASTM D-790	1770	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	HDT	ASTM D648/ISO 75	71	℃（℉）
Vicat softening temperature		ASTM D1525/ISO R306	80	℃（℉）
Combustibility	垂直燃烧性	UL -94	1.5mmHB
Hot deformation temperature	6.4mm,1.82MPa	ASTM D-648	71	°C
Vicat softening temperature	5kg	JIS K-7206	80	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
density		ASTM D792/ISO 1183	1.10
Shrinkage rate		ASTM D955	3-5	%
melt mass-flow rate		ASTM D1238/ISO 1133	1.4	g/10min
Total Light Transmittance	2mmt	ASTM D-1003	90.5	%
turbidity	2mmt	ASTM D-1003	1.5	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.