Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| melt mass-flow rate | | ISO 1133 | 22 g/10min |
| Shrinkage rate | | Internal Method | 1.4-1.8 % |
| melt mass-flow rate | | ISO1133 | 22 g/10min |
| Shrinkage rate | | 内部方法 | 1.4到1.8 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ISO2039-2 | 76 |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| Haze ratio | | ISO14782 | 30 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO 527-2 | 950 Mpa |
| Yield tensile stress | | ISO 527-2 | 27 Mpa |
| Fracture tensile strain | | ISO 527-2 | 17 % |
| Flexural modulus | | ISO 178 | 950 Mpa |
| bending strength | | ISO 178 | 29 Mpa |
| Fracture rate | | ISO 527-2 | 200 % |
| Fracture rate | | ISO 179 | 6.0 kJ/m² |
| Fracture rate | | ISO 2039-2 | 76 |
| Tensile modulus | | ISO527-2 | 950 Mpa |
| Tensile stress | | ISO527-2 | 27.0 Mpa |
| Tensile strain | | ISO527-2 | 17 % |
| Nominal tensile fracture strain | | ISO527-2 | 200 % |
| Flexural modulus | | ISO178 | 950 Mpa |
| Bending stress | | ISO178 | 29.0 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO179 | 6.0 kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO75-2/B | 78.0 °C |
| Fracture rate | Test Condition | Test Method | Test Result |
|---|
| Thermal performance | | ISO 75-2/B | 78 °C |
| optical performance | | ISO 14782 | 30 % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.