LLDPE FS250B SUMITOMO JAPAN

Properties:
High mobility
Good liquidity
High transparency
High toughness
Processability
Usages:
film
Electric wire
Cable Applications
Stretch winding
cast film
Compare

Technical Data Sheet

physical property	Test Condition	Test Method	Test Result
melt mass-flow rate		ASTM D1238	2.2 g/10min

optical performance	Test Condition	Test Method	Test Result
gloss		ASTM D2457	50
gloss	gloss		ASTM D2457	145
Haze ratio		ASTM D1003	20 %
Haze ratio	Haze ratio		ASTM D1003	0.60 %

Mechanical properties	Test Condition	Test Method	Test Result
coefficient of friction		ASTM D1894	>0.51

film	Test Condition	Test Method	Test Result
film thickness			30 µm
Secant modulus -1% Decant, MD		ASTM D882	205 Mpa
Secant modulus -1% Decant, MD	Secant modulus -1% Decant, MD		ASTM D882	150 Mpa
Secant modulus -1% Decant, TD		ASTM D882	150 Mpa
Secant modulus -1% Decant, TD	Secant modulus -1% Decant, TD		ASTM D882	255 Mpa
tensile strength		ASTM D882	35.0 Mpa
	tensile strength		ASTM D882	50.0 Mpa
		tensile strength		ASTM D882	30.0 Mpa
		tensile strength	tensile strength		ASTM D882	30.0 Mpa
elongation		ASTM D882	770 %
film thickness			20 µm
elongation		ASTM D882	620 %
Tensile strain		ASTM D882	930 %
Tensile strain	Tensile strain		ASTM D882	940 %
Dart impact		ASTM D1709	90 g
Dart impact	Dart impact		ASTM D1709	75 g
Elmendorf tear strength		ASTM D1922	130 g
	Elmendorf tear strength		ASTM D1922	60 g
		Elmendorf tear strength		ASTM D1922	350 g
		Elmendorf tear strength	Elmendorf tear strength		ASTM D1922	240 g

Thermal performance	Test Condition	Test Method	Test Result
melting temperature		DSC	122 °C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.