Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792 | 1.70 g/cm³ |
| melt mass-flow rate | | ASTM D1238 | 7.0to10 g/10min |
| Water absorption rate | Equilibrium | ASTM D570 | <0.10 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | | ASTM D2240 | 74 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| Limiting Oxygen Index | | ASTM D2863 | >52 % |
| UL flame retardant rating | | UL 94 | V-0 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ASTM D882 | 1320 MPa |
| tensile strength | | ISO 527-3 | 28.5 MPa |
| tensile strength | | ISO 527-3 | 41.4 MPa |
| elongation | | ISO 527-3 | 5.0 % |
| elongation | | ISO 527-3 | 310 % |
| coefficient of friction | Itself - Dynamic | ASTM D1894 | 0.20 |
| Taber abraser | | ASTM D4060 | 16.5 mg |
| film | Test Condition | Test Method | Test Result |
|---|
| Tear strength of pants shape | | DIN 53363 | 420.0 kN/m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| dielectric strength | | ASTM D149 | 14 kV/mm |
| dielectric constant | | ASTM D150 | 2.57 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Fusion temperature | | ASTM D3418 | 24.0 J/g |
| thermal stability | | TGA | 359 °C |
| brittle temperature | | ASTM D746A | <-50.0 °C |
| Glass Transition Temperature | | DMA | 70.0 °C |
| melting temperature | | ASTM D3418 | 200 °C |
| Crystallization peak temperature | | ASTM D3418 | 180 °C |
| thermal conductivity | | ASTMC177 | 0.18 W/m/K |
| Crystallization peak temperature | | ASTM D3418 | 22.7 J/g |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.