PP RPP 2000 A SCHULMAN USA

Form：Granules | Grade：Halogen-free flame retardant grade

Properties:

Halogen-free

Supplier(1)

Product Description

Certificates(1)

Datasheet

Product Description

Properties:

Halogen-free

Certificates

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	17	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	NoBreak
flammability	Test Condition	Test Method	Test Result	Test Unit
Extreme Oxygen Index		ISO 4589-2	27	%
Hot filament ignition temperature	3.0mm	IEC 60695-2-13	725	°C
	Hot filament ignition temperature	1.5mm	IEC 60695-2-13	725	°C
	Hot filament ignition temperature	Hot filament ignition temperature	0.75mm	IEC 60695-2-13	725	°C
Burning wire flammability index	3.0mm	IEC 60695-2-12	960	°C
	Burning wire flammability index	1.5mm	IEC 60695-2-12	960	°C
	Burning wire flammability index	Burning wire flammability index	0.75mm	IEC 60695-2-12	960	°C
UL flame retardant rating	3.0mm	IEC 60695-11-10,-20	V-2
	UL flame retardant rating	1.5mm	IEC 60695-11-10,-20	V-2
		UL flame retardant rating	0.75mm	IEC 60695-11-10,-20	V-2
			UL flame retardant rating	3.0mm	UL 94	V-2
				UL flame retardant rating	1.5mm	UL 94	V-2
				UL flame retardant rating	UL flame retardant rating	0.75mm	UL 94	V-2
Burning rate	3.00mm,自动灭火	ISO 3795	0.0	mm/min
	Burning rate	1.50mm,自动灭火	ISO 3795	0.0	mm/min
	Burning rate	Burning rate	0.750mm,Self-Extinguishing	ISO 3795	0.0	mm/min
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus		ISO 527-2/1A/1	1800	Mpa
tensile strength	Yield	ISO 527-2/1A/50	38.0	Mpa
Tensile strain	Yield	ISO 527-2/1A/50	8.0	%
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/Bf	102	°C
RTI Str	3.0mm	UL 746	65.0	°C
	RTI Str	1.5mm	UL 746	65.0	°C
	RTI Str	RTI Str	0.75mm	UL 746	65.0	°C
RTI Imp	3.0mm	UL 746	65.0	°C
	RTI Imp	1.5mm	UL 746	65.0	°C
	RTI Imp	RTI Imp	0.75mm	UL 746	65.0	°C
RTI Elec	3.0mm	UL 746	65.0	°C
RTI Elec	RTI Elec	1.5mm	UL 746	65.0	°C
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/Af	59.0	°C
Vicat softening temperature	--	ISO 306/A50	157	°C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B50	97.0	°C
Ball Pressure Test	145°C	IEC 60695-10-2	Pass
RTI Elec	0.75mm	UL 746	65.0	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Melt Volume Flow Rate (MVR)	230°C/2.16kg	ISO 1133	8.00	cm3/10min
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Compared to the anti leakage trace index		IEC 60112	PLC 0

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.