Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO1183 | 1.60 g/cm³ |
| Apparent density | | ISO60 | 0.72 g/cm³ |
| Shrinkage rate | | ISO2577 | 0.20 % |
| Water absorption rate- | | ISO62 | 15.0 mg |
| PostShrinkage | | ISO2577 | 0.15 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| | ISO2039-1 | 250 MPa |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| CompressionMoldingPressure | | | >15.0 MPa |
| CompressionMoldingTemperature | | | 160到190 °C |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| compression stress | | ISO604 | 250 MPa |
| Tensile modulus | | ISO527-2/1 | 10500 MPa |
| Tensile stress | | ISO527-2/5 | 85.0 MPa |
| Flexural modulus | | ISO178 | 10000 MPa |
| Bending stress | | ISO178 | 135 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO179/1eA | 3.5 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO179/1eU | 15 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC60093 | 1E+11 ohms |
| Volume resistivity | | IEC60093 | 1E+12 ohms·cm |
| dielectric strength | | IEC60243-1 | 23 kV/mm |
| | IEC60250 | 7.00 |
| Dissipation Factor | | IEC60250 | 0.10 |
| CTI | | IEC60112 | 150 V |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO75-2/C | 170 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.