Polyester, TS

Polyester, TS Menzolit® SMC 0410 Menzolit Ltd (UK)

Compare

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength	Compression Molded	ISO 179	86 kJ/m²

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	3.0mm	UL 94	HB

mechanical properties	Test Condition	Test Method	Test Result
tensile strength	Yield,Compression Molded	ISO 527-2	90.0 MPa
Tensile strain	Break,Compression Molded	ISO 527-2	1.5 %
Bending modulus	Compression Molded	ISO 178	11000 MPa
Tensile modulus	Compression Molded	ISO 527-2	12000 MPa
bending strength	Compression Molded	ISO 178	190 MPa
Compressive stress		ISO 14126	100 MPa
Poisson's ratio		Internal Method	0.30
MatrixCrazingStrain		Internal Method	0.40 %

thermal performance	Test Condition	Test Method	Test Result
Glass transition temperature		DSC	200 °C
Linear coefficient of thermal expansion	MD	ISO 11359-2	1E-05 cm/cm/°C
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	>200 °C
Continuous use temperature		Internal Method	165 °C

Physical properties	Test Condition	Test Method	Test Result
density		ISO 1183	1.90 g/cm³
Shrinkage rate	--	ISO 2577	-0.050 %
Shrinkage rate	Shrinkage rate	--2	DIN 53464	0.0 %
Water absorption rate	Saturation,23°C	ISO 62	<0.50 %

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.