PA66 TAROMID A 280 G5 Taro Plast S.p.A.

Properties:

Filler glass fiber reinforced material 25% filler by weight

Product Description

Certificates(0)

Datasheet

Product Description

Properties:

Filler | glass fiber reinforced material | 25% | filler by weight

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Charpy Notched Impact Strength	23°C	ASTMD256	6.0	kJ/m²
Impact strength of simply supported beam without notch	23°C	ASTMD256	36	kJ/m²
Impact strength of cantilever beam gap	23°C,3.20mm	ISO 180	70	J/m
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	0.750mm	UL 94	HB
Hot filament ignition temperature	2.00mm	IEC 60695-2-13	750	°C
Extreme Oxygen Index		ASTM D2863	26	%
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
elongation	Break	ASTMD638	3.0	%
Bending modulus		ASTMD790	8500	MPa
crack		ASTM D790	230	MPa
Tensile modulus		ASTMD638	8800	MPa
tensile strength	Break	ASTMD638	146	MPa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Continuous use temperature	--4	IEC 60216	130	°C
Continuous use temperature	Continuous use temperature	--5	IEC 60216	140	°C
Linear coefficient of thermal expansion	MD：-30to30°C	ASTM D696	3.5E-05	cm/cm/°C
Continuous use temperature	--6	IEC 60216	180	°C
Vicat softening temperature		ISO 306/B50	250	°C
Ball Pressure Test	165°C	VDE0470	Pass
Melting temperature		ASTMD211	256	°C
Continuous use temperature	--3	IEC 60216	100	°C
Hot deformation temperature	1.8MPa,Unannealed	ASTMD648	238	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
density		ASTMD792	1.30to1.32	g/cm³
melt mass-flow rate	280°C/2.16kg	ASTMD1238	15	g/10min
Shrinkage rate	MD	ASTM D955	0.40to0.50	%
Shrinkage rate	Shrinkage rate	TD	ASTM D955	1.0to1.4	%
saturated		ASTM D570	5.5	%
saturated	saturated		ISO 62	5.5	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Volume resistivity		ASTM D257	8E+15	ohms·cm
Dielectric strength	2.00mm	ASTM D149	24	kV/mm
Compared to the anti leakage trace index	SolutionA	IEC 60112	PLC 1
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	R-Scale	ASTM D785	120

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.