Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| MediumDensity | | | 1.14 g/cm³ |
| Water absorption rate | | ISO62 | 0.90 % |
| Water absorption rate | | ISO62 | 0.35 % |
| density | | ISO1183 | 1.34 g/cm³ |
| melt mass-flow rate | | ISO1133 | 2.0 g/10min |
| Melt volume flow rate | | ISO1133 | 1.70 cm3/10min |
| Shrinkage rate | | ISO294-4 | 1.4 % |
| Shrinkage rate | | ISO294-4 | 1.3 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ISO2039-2 | 58 |
| Rockwell hardness | | ISO2039-2 | 105 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| Burning rate 3 | | ISO3795 | 41 mm/min |
| UL flame retardant rating | | UL94 | HB |
| Flammability level | | IEC60695-11-10,-20 | HB |
| FMVSS flammability | | FMVSS302 | B |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| Emission | | VDA275 | <8.00 mg/kg |
| Emissions of Organic Compounds | | VDA277 | 2.90 µgC/g |
| SpecificWear | | ASTMD1894 | 60.0 10^-6mm³/N·m |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO527-2 | 1400 Mpa |
| Tensile stress | | ISO527-2 | 41.0 Mpa |
| Tensile strain | | ISO527-2 | 30 % |
| Nominal tensile fracture strain | | ISO527-2 | >50 % |
| TensileCreepModule | | ISO899-1 | 1100 Mpa |
| Tensile creep modulus | | ISO899-1 | 550 Mpa |
| Flexural modulus | | ISO178 | 1100 Mpa |
| Bending stress | | ISO178 | 34.0 Mpa |
| Coefficient of Friction | | ASTMD1894 | 0.32 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO179/1eA | 18 kJ/m² |
| Charpy Notched Impact Strength | | ISO179/1eA | 90 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO179/1eU | NoBreak |
| Impact strength of simply supported beam without notch | | ISO179/1eU | NoBreak |
| Impact strength of cantilever beam gap | | ISO180/1A | 20 kJ/m² |
| Impact strength of cantilever beam gap | | ISO180/1A | 90 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| | IEC60250 | 4.40 |
| | IEC60250 | 3.80 |
| CTI | | IEC60112 | 600 V |
| Surface Resistivity | | IEC60093 | 1E+14 ohms |
| Volume resistivity | | IEC60093 | 1E+14 ohms·cm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO75-2/A | 60.0 °C |
| Glass transition temperature 2 | | ISO11357-2 | -35.0 °C |
| melting temperature | | ISO11357-3 | 178 °C |
| | ISO11359-2 | 1.3E-04 cm/cm/°C |
| | ISO11359-2 | 1.4E-04 cm/cm/°C |
| AnnealingTemperature | | | 160 °C |
| AnnealingTime-Optional | | | 30.0 min/mm |
| EffectiveThermal Diffusivity | | | 6E-08 m²/s |
| | ISO75-2/B | 100 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.