| other | Test Condition | Test Method | Test Result |
|---|
| purpose | | | 管道涂覆,电缆料,内衬,农膜,重载膜,重载收缩膜 |
| Basic performance | Test Condition | Test Method | Test Result |
|---|
| density | | | 0.917-0.921 g/cm³ |
| melt mass-flow rate | | | 0.2-0.5 g/10min |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| gloss | | ASTM D-2457 | >8 |
| ultimate elongation | | ISO 527 | >150 % |
| ultimate elongation | | ISO 527 | >500 % |
| Elastic modulus (tensile) | | ISO 527 | >180 n/mm² |
| Yield tensile strength | | ISO 527 | >8 n/mm² |
| ultimate tensile strength | | ISO 527 | >20 Mpa |
| ultimate tensile strength | | ISO 527 | >15 Mpa |
| Other performance | Test Condition | Test Method | Test Result |
|---|
| Falling dart | | ASTM D-1709 | >150 g |
| turbidity | | ASTM D-1003 | ＜20 % |
| film thickness | | | 70 µm |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| | IEC 93 | >1.E15 Ω.cm |
| dielectric constant | | IEC 250 | >2 |
| Physical properties | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792/ISO 1183 | 0.920 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| vicat | | ISO 306 | >90 °C |
| melting temperature | | ISO 3146 | >104 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.